EXTRUDED MILL FINISHED ALUMINIUM PROFILES

Aluminium extrusions in 6000 series alloy are approximately 97.23% to 98.94% primary aluminium by mass, with alloying elements composing the remaining mass percent.

Density 2.64 - 2.84 (kg/m3)x 10^3

Melting point (typical) 476.7 - 657.2 C

Electrical conductivity (typical) 27 - 62 (Ms/m) x (5.8x10^10 x &IACS)

Thermal conductivity (typical) 12.08-24.34 W/m.K

Average coefficient of thermal expansion (typical) 20°C to 100°C / 68°F to 212°F 22.3 - 23.9 per C

Modulus of elasticity (typical) 69 - 73 MPa x 10^3

Hardness (typical) 3 - 17 Webster-B

Yield strength (min) 60 - 330 MPa

Ultimate tensile strength (min) 120 - 370 MPa

Breaking elongation (min) > 6 %

Chemical composition Varying by alloy,Al 97.23% - 98.94%